High Quliafied Low Priced UHMW-PE Skating Rink Fence

Jul 18, 2019
Basic Info
  • Kind: White Plastic Sheet

  • Contraction Percentage: <0.4%

  • Size: as Your Request

  • Thickness: 6-350mm

  • Specification: ISO 9001: 2008

  • HS Code: 3920109090

  • Material: PE

  • Water Absorption: <0.01%

  • Tensile Strength: (30~40)MPa

  • Density: 0.98-1.0g/Cm3

  • Transport Package: Carton Plus Stretch Film, Pallets, Wood Packaging

Product Description
Detailed description:                                                                                                       
fence plate of ice hockey rink: around the  ice hockey rink is 1.15m-1.22m high solid wall made of UHMW-PE composite material. In addition to the formal  markers in field, all  the ice surface  and  the  inner  wall  of  the  wall  should  be  white.

Product characteristic:                                                                                                    
1. the abrasion performance of the UHMW-PE coaming ranks first in the plastic, while molecular weight is greater,  the abrasion resistance and impact resistance of the material is higher .
2. The impact strength of ultra high molecular weight polyethylene coaming is the highest value in the existing plastic, even in 70 degrees it still has very high impact strength;
3. Self lubrication, friction coefficient is small, save energy, feel like wax
4. it has extremely low water absorption. Therefore, its physical and mechanical properties is irrelevant to the moisture factor that in the use of the working conditions.
5. Chemical property of UHMW-PE is stable, in a certain temperature and concentration range, it is able to endure corosion of  acid, alkali, salt and other corrosive medium or organic solvent.
6. Ultra high molecular weight polyethylene board is tasteless, non-toxic, odorless, and itself is non corrosive, it has physiological circulation and physiological adaptability.

 Technical date                                                                                            
break elongation rate:238
molecular weight :2 million -1020 million
thickness :10--300(mm)
Delivery pointunlimited  
tensile breaking strength:40 mPa
Tensile yield strength :21 mPa
density:0.98 g/cm3
Notched impact strength :100-160 kgcm/cm2
heat distortion temperature :100 oC
melting point :160 oC
melt flow rate :unlimited   g/10min
Flexural modulus :600 mPa
Vicat softening point :132 oC
functional level :Board level