LDPE LDPE Granules Low Density Polyethylene

Jul 15, 2019
Basic Info
  • Usage: General Plastics, Engineering Plastics, Specialty Plastics

  • Plastic Forming Method: Film Pressure

  • Density: 0.920-0.922g/cm3

  • Turbidity: 10.0%

  • Tensile Strength (Horizontal): 20n/Mm

  • Breaking Strength: 9.0mpa

  • Colour: White

  • Trademark: Low Density Polyethylene(LDPE)

  • Specification: SGS

  • Material: Low Density Polyethylene/LDPE

  • Plastic Properties After Heated: Thermoplastic Plastics

  • Color: White

  • Mfr(Melt Flow Rate): 2.1-2.9g/10min

  • Elongation at Break: 500

  • Tensile Strength (Vertical): 50n/Mm

  • Cleanness: 7/Kg

  • Grade: Injection ,Film Grade

  • Transport Package: 25kg/Bag, 20mt/20′fcl

  • Origin: Heibei, China


Product Description

Specifications

Direct Manufacturer, Free Sample, Competitive Price and Good quality LDPE for sale

Usage: General Plastics
Material: Low Density Polyethylene/LDPE
Color: White

Product Description
Low Density Polyethylene
Product name: Low Density Polyethylene
Other name: LDPE
CAS No.: 9002-88-4

Character: High density polyethylene for non-toxic, tasteless, no smelly white particles, melting point is about 130 ° C, relative density of 0.915 ~ 0.940. It has good heat resistance and cold resistance, chemical stability, but also has high rigidity and toughness, good mechanical strength. Dielectric properties, environmental stress cracking resistance sex also is good

Application:
1. Fiber (Carpet, Textiles, Upholstery, etc. )
2. Film (Shopping bags, casting film, multilayer film, etc. )
3. Blow Molding (Medical & Cosmetic container, Lubricant & Paint container, etc)
4. Extrusion Molding (Sheet, Pipe, Wire & Cable, etc. )
5. Injection Molding (Automotive, Electronic, Construction, House wares, Furniture, Toys, etc. )

Quality index: Different grade
Item: Standard
Density: (g/cm3)0.922
Tension strength/Mpa: 130
Elongation/%: 1000
Embitterment temperature ° C: -35
Melting Point/° C: 110
Elongation%: ≥ 600
Tensile strength: ≥ 130
The melt flow index: 0.3
FTU%: ≤ 13%
TestsValueUnit
Melt Flow Rate   (MFR)15g/10min
Density0.922g/cm3
Tensile Yield   Strength7Mpa
Elongation at Break75%
Wien Softening   Point85°C
PackingIn 25 kg PP woven bags,20MT/20'FCL

LDPE film grade
 
TestsValueUnit
Melt Flow Rate   (MFR)2g/10min
Density0.9225g/cm3
Tensile Strength9Mpa
Elongation at Break500%
Fish eye   max(0.3-2mm)30n/1200cm2
Stripes20cm/20m3
PackingIn 25 kg PP woven bags,20MT/20'FCL